PolyOne Maxxam™ PPC-40T Nat Polypropylene Copolymer (PP Copolymer)

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer PolyOne Corporation
Trade Name Maxxam™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Maxxam™ PPC-40T Nat Polypropylene Copolymer (PP Copolymer).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
ASTM D955
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Procedure A; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 70
70
ASTM D785
Tensile Strength, Yield 23.4 MPa
3390 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 25 %
25 %
Type I, 51 mm/min; ASTM D638
Flexural Strength 41.4 MPa
6000 psi
ASTM D790
Flexural Modulus 2.96 GPa
429 ksi
ASTM D790
Izod Impact, Notched 0.270 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
0.506 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Izod Impact, Unnotched 2.20 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
4.12 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256
Gardner Impact 4.86 J

@Thickness 3.18 mm,
Temperature -23.0 °C
3.58 ft-lb

@Thickness 0.125 in,
Temperature -9.40 °F
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 129 °C

@Thickness 3.18 mm
264 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Mold Temperature 16.0 - 50.0 °C
60.8 - 122 °F
Descriptive Properties Value Comments
Additive Impact Modifier
Appearance Natural Color
Features Copolymer
General Purpose
Impact Modified
Filler / Reinforcement Talc Filler
Unspecified FillerReinfor., 40% Filler by Weight
Forms Pellets
Generic Material PP Copolymer
Generic Name Polypropylene Copolymer (PP Copolymer)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Automotive Applications
Construction Applications
Consumer Applications
General Purpose
Industrial Applications