Material Notes:

Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings.*NOTE: HARDNESS DATA IS BASED ON SINGLE LOT DATA.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	0.998 g/cc	0.998 g/cc	ASTM D792
Melt Flow	0.91 - 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C	0.91 - 2.7 g/10 min @Load 4.76 lb, Temperature 374 °F	Procedure A; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	65	65	10 sec; ASTM D2240
	66	66	ASTM D2240
Tensile Strength, Yield	20.7 MPa	3000 psi	Type I, 51 mm/min; ASTM D638
Elongation at Break	500 %	500 %	Type I, 51 mm/min; ASTM D638
Flexural Modulus	0.276 GPa	40.0 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	67.0 °C @Thickness 3.18 mm	153 °F @Thickness 0.125 in	Annealed; ASTM D648
Flammability, UL94	V-2 @Thickness 0.750 mm	V-2 @Thickness 0.0295 in	NC; UL 94
Oxygen Index	27 % @Thickness 3.18 mm	27 % @Thickness 0.125 in	ASTM D2863

Descriptive Properties	Value	Comments
Additional Information	*NOTE: HARDNESS DATA IS BASED ON SINGLE LOT DATA.
Features	Flame Retardant
Forms	Pellets
Generic Material	HDPE
Generic Name	Polyethylene, High Density (HDPE)
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant