PolyOne LubriOne™ AT-000/05T 2S Acetal (POM) Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | PolyOne Corporation |
| Trade Name | LubriOne™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne LubriOne™ AT-000/05T 2S Acetal (POM) Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.020 - 0.025 cm/cm | 0.020 - 0.025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.3 MPa | 7010 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 25 - 30 % | 25 - 30 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 0.586 GPa | 85.0 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.29 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C @Thickness 6.35 mm |
307 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.9 °C @Thickness 6.35 mm |
192 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Copolymer | |
| Lubricated | ||
| Forms | Pellets | |
| Generic Material | Acetal (POM) Copolymer | |
| Generic Name | Acetal (POM) Copolymer | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| South America | ||
| RoHS Compliance | RoHS Compliant | |
| Uses | Appliance Components | |
| Conveyor Parts | ||
| Printer Parts |