- PolyOne Lubri-Tech™ SY-000/05T High Impact Styrene - 5% PTFE (discontinued **)
PolyOne Lubri-Tech™ SY-000/05T High Impact Styrene - 5% PTFE (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, PTFE Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ SY-000/05T High Impact Styrene - 5% PTFE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm |
0.0050 - 0.0070 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 4.0 - 8.0 % | 4.0 - 8.0 % | ASTM D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ASTM D638 |
| Flexural Yield Strength | 31.0 MPa | 4500 psi | ASTM D790 |
| Flexural Modulus | 2.59 GPa | 376 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 - 1.07 J/cm @Thickness 6.35 mm |
1.50 - 2.00 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 232 °C | 410 - 450 °F | Stock |
| Mold Temperature | 49.0 - 71.0 °C | 120 - 160 °F | |
| Drying Temperature | 49.0 - 66.0 °C | 120 - 151 °F |