- PolyOne Lubri-Tech™ PF-30CF/15T Polysulfone, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
PolyOne Lubri-Tech™ PF-30CF/15T Polysulfone, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PF-30CF/15T Polysulfone, Carbon Fiber Reinforced, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.472 g/cc | 1.472 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 100 ohm-cm | 10 - 100 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10 - 100 ohm | 10 - 100 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 382 °C | 670 - 720 °F | Molding |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 135 - 149 °C | 275 - 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- MV Labs PT167 Li2Pt(CN)4·xH2O Lithium tetracyanoplatinate(II) hydrate
- Niche Polymer PPHG20BK Homopolymer PP, 20% Glass Fiber Filled
- Kazanorgsintez 107-277 Low Density Polyethylene Composition with Improved Processibility
- Kotec Carbotex KGN-15MRA Polycarbonate, Flame Retardant, 15% Glass Fiber Reinforced
- LG Chemical PB900 PVC
- KaMin FIBEREX®
- Shuman 310 Utility Black PC/ABS Alloy
- A. Schulman POLYFORT™ PP 3719 Impact Copolymer Polypropylene
- Total Lumicene® MR 2001 Polypropylene, Metallocene Polypropylene
- Cheng Yu Plastic 3276 TPE Rubber
Copyright © lookpolymers.com All Rights Reserved