- PolyOne Lubri-Tech™ NL-30CF/15T Nylon 6/12, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
PolyOne Lubri-Tech™ NL-30CF/15T Nylon 6/12, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ NL-30CF/15T Nylon 6/12, Carbon Fiber Reinforced, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:PTFE LubricatedLow WearCarbon Fiber ReinforcedHigh StiffnessProcessing Method:MoldingPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 193 MPa | 28000 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 24.1 GPa | 3500 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 286 MPa | 41500 psi | ASTM D790 |
| Flexural Modulus | 15.34 GPa | 2225 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |