PolyOne Lubri-Tech™ MP-000/15T Modified PPO - 15% PTFE  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, PTFE Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Lubri-Tech™ MP-000/15T Modified PPO - 15% PTFE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D792
Water Absorption 0.20 %
0.20 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm

@Thickness 3.17 mm
 0.0060 - 0.0080 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 50.0 MPa
7250 psi
ASTM D638
Elongation at Break 1.0 - 5.0 %
1.0 - 5.0 %
ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
ASTM D638
Flexural Yield Strength 69.0 MPa
10000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 0.640 - 1.01 J/cm

@Thickness 6.35 mm
 1.20 - 1.89 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 601 °F
Stock
Mold Temperature 121 °C
250 °F
Drying Temperature 121 °C
250 °F