PolyOne Lubri-Tech™ AT-000/15T-2S Copolymer Acetal - 15% PTFE, 2% Silicone Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-000/15T-2S Copolymer Acetal - 15% PTFE, 2% Silicone Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.022 cm/cm @Thickness 3.17 mm |
0.022 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 60 | 60 | ASTM D785 |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D638 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 6.35 mm |
0.993 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 99.0 µm/m-°C @Temperature 20.0 °C |
55.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | Cenco test |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | Stock |
| Mold Temperature | 49.0 - 82.0 °C | 120 - 180 °F | |
| Drying Temperature | 82.0 °C | 180 °F |