PolyOne Geon™ Vinyl Wire & Cable W9400L Polyvinyl Chloride, Flexible (PVC, Flexible)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Wire and Cable Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Vinyl Wire & Cable W9400L Polyvinyl Chloride, Flexible (PVC, Flexible).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore D 35
35
15 sec; ASTM D2240
Tensile Strength, Yield 20.0 MPa
2900 psi
Type IV, 510 mm/min; ASTM D638
Elongation at Break 340 %
340 %
Type IV, 510 mm/min; ASTM D638
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 105 °C
221 °F
UL Temperature Rating
Brittleness Temperature -18.9 °C
-2.02 °F
ASTM D746
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
ALL; UL 94
Oxygen Index 30 %

@Thickness 3.18 mm
30 %

@Thickness 0.125 in
ASTM D2863
Processing Properties Metric English Comments
Melt Temperature 182 - 188 °C
360 - 370 °F
Descriptive Properties Value Comments
Features Flame Retardant
Forms Pellets
Generic Material PVC, Flexible
Generic Name Polyvinyl Chloride, Flexible (PVC, Flexible)
Processing Method Extrusion
Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Retention of Tensile Elongation 90%
136°C, 508.0 µm; 168 hr, UL Standard
Retention of Tensile Strength 110%
136°C, 508.0 µm; 168 hr, UL Standard
RoHS Compliance RoHS Compliant
Uses Wire & Cable Applications