PolyOne Geon™ Vinyl Rigid Molding M4910 (USP CLASS VI for TRANS 9494 only) Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Molding M4910 (USP CLASS VI for TRANS 9494 only) Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 73.7 cm | 29.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | ASTM D2240 |
| Tensile Strength, Yield | 54.5 MPa | 7900 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 19 % | 19 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.91 GPa | 422 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 85.5 MPa | 12400 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
0.993 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Injection Molded; ASTM D256A |
| 0.800 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 °C @Thickness 6.35 mm |
149 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
| 67.8 °C @Thickness 6.35 mm |
154 °F @Thickness 0.250 in |
Unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C @Thickness 6.35 mm |
142 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 62.2 °C @Thickness 6.35 mm |
144 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 204 °C | 390 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | USP Class VI | |
| Appearance | Clear/Transparent | |
| Features | Medium Flow | |
| Radiation (Gamma) Resistant | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- Network Polymers NPP 20-3401
- Kazanorgsintez 158-280 Low Density Polyethylene Composition with Improved Processibility
- SABIC Innovative Plastics LNP STAT-KON EX11402 PEI
- SSAB Tunnplat Docol® 1000 DL High-strength Steel
- Von Roll Isola IMI Varnish 716 Solventless Polyester Varnish for Electrical Insulation
- Barlog Plastics KEBAFLEX S 35 A.01 TPE-S, Shore A35, translucent
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- E-Polymers SEPAZ® C245GP 45% Glass Fiber Reinforced LCP Resin
Copyright © lookpolymers.com All Rights Reserved