PolyOne Geon™ Vinyl Rigid Molding M3890 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Molding M3890 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 91.4 cm | 36.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | ASTM D2240 |
| Tensile Strength, Yield | 43.4 MPa | 6290 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 43 % | 43 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 68.9 MPa | 9990 psi | ASTM D790 |
| Flexural Modulus | 2.42 GPa | 351 ksi | ASTM D790 |
| Izod Impact, Notched | 5.90 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
11.1 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Injection Molded; ASTM D256A |
| 6.40 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C @Thickness 6.35 mm |
160 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 75.0 °C @Thickness 6.35 mm |
167 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C @Thickness 6.35 mm |
154 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 72.2 °C @Thickness 6.35 mm |
162 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746 |
| Flammability, UL94 | V-0 @Thickness 1.40 mm |
V-0 @Thickness 0.0551 in |
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 210 °C | 390 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Opaque | |
| Features | General Purpose | |
| High Flow | ||
| High Impact Resistance | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Appliances | |
| Business Equipment | ||
| Construction Applications | ||
| Electrical/Electronic Applications | ||
| General Purpose | ||
| Telecommunications |
Users viewing this material also viewed the following:
- Resinoid 1363 Phenolic Molding, Glass Reinforced
- MarkeTech Yttrium Aluminate (YAlO3) Single Crystal Substrate
- Momentive Performance Materials RTV6136 Potting/Encapsulating Gel
- SABIC Innovative Plastics NORYL NF1030 PPE+PS (Asia Pacific)
- A. Schulman SCHULAMID® 66 MV3 Unreinforced Nylon 6/6
- A. Schulman POLYBATCH™ Blue 4535 Concentrate Based In Polyethylene
- Cossa Polimeri ESTABLEND PA 6000 ABS / Nylon 6 Blend
- Epoxy Technology EPO-TEK® 353ND-T4 Thixotropic Epoxy
- AlphaGary Evoprene™ 003 Standard SBS Thermoplastic Elastomer Compound
Copyright © lookpolymers.com All Rights Reserved