PolyOne Geon™ Vinyl Rigid Extrusion 87345 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87345 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.99 GPa | 434 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 98.6 MPa | 14300 psi | ASTM D790 |
| Flexural Modulus | 3.19 GPa | 463 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.11 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 0.640 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| 0.800 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 69.4 J/cm @Temperature 23.0 °C |
0.130 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 199 J/cm @Temperature 23.0 °C |
0.373 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C | 33.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C @Thickness 3.18 mm |
168 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Good | |
| Features | Good Chemical Resistance | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 13454 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Piping |
Users viewing this material also viewed the following:
- MV Labs AG100 AgC2H3O2 Silver acetate
- PolyOne Elastamax™ EG-9172 Thermoplastic Elastomer (TPE)
- Ferro EG 2791 Thick Film Glass
- Indium Corp. 1081-T Wave Solder Flux
- Materion Brush 1915â„¢ Heat Treated Temper Wire, 0.375" - 0.500"
- Henkel Frekote B-15 Sealer Mold Sealer
- DuPont Teijin Films Mylar® MDA Polyester Film, 92 Gauge
- Techmer ES HiFill® PP LGF40 CC HS BK 40% Glass Filled
Copyright © lookpolymers.com All Rights Reserved