PolyOne Geon™ Vinyl Rigid Extrusion 8700A Polyvinyl Chloride, Rigid (PVC, Rigid)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Vinyl Rigid Extrusion 8700A Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Note: Automotive OEM approval(s). Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this product. Note: The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Rockwell R 111
111
ASTM D785
Hardness, Shore D 78
78
15 sec; ASTM D2240
Tensile Strength, Yield 42.7 MPa
6190 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 2.69 GPa
390 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 75.8 MPa
11000 psi
ASTM D790
Flexural Modulus 2.62 GPa
380 ksi
ASTM D790
Compressive Strength 55.8 MPa
8090 psi
ASTM D695
Izod Impact, Notched 0.590 J/cm

@Thickness 3.18 mm,
Temperature -18.0 °C
1.11 ft-lb/in

@Thickness 0.125 in,
Temperature -0.400 °F
Compression Molded; ASTM D256A
0.850 J/cm

@Thickness 3.18 mm,
Temperature 0.000 °C
1.59 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
Compression Molded; ASTM D256A
9.10 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
17.0 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded; ASTM D256A
Dart Drop Total Energy 35.6 J/cm

@Temperature 23.0 °C
0.0667 ft-lb/mil

@Temperature 73.4 °F
Procedure A, C.125; ASTM D4226
35.6 J/cm

@Temperature 23.0 °C
0.0667 ft-lb/mil

@Temperature 73.4 °F
Procedure B, C.125; ASTM D4226
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 67.0 µm/m-°C
37.2 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 72.8 °C

@Thickness 3.18 mm
163 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.711 mm
V-0

@Thickness 0.0280 in
ALL; UL 94
V-0

@Thickness 0.870 mm
V-0

@Thickness 0.0343 in
All Colors
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
ALL; UL 94
Electrical Properties Metric English Comments
Dielectric Constant 3.3

@Frequency 1000 Hz
3.3

@Frequency 1000 Hz
ASTM D150
3.9

@Frequency 60.0 Hz
3.9

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 27.0 kV/mm
686 kV/in
ASTM D149
Dissipation Factor 0.029

@Frequency 60.0 Hz,
Temperature 30.0 °C
0.029

@Frequency 60.0 Hz,
Temperature 86.0 °F
24 hr; ASTM D150
0.040

@Frequency 1000 Hz,
Temperature 30.0 °C
0.040

@Frequency 1000 Hz,
Temperature 86.0 °F
24 hr; ASTM D150
Processing Properties Metric English Comments
Melt Temperature 179 - 182 °C
354 - 360 °F
Descriptive Properties Value Comments
Agency Ratings NSF 51
NSF 61
Automotive Specifications CHRYSLER MS-DC28 Type B CPN2647 Color: Black
GM GM7001M (PVC)
Ease of Sizing Excellent
Features General Purpose
Good Dimensional Stability
Good Melt Strength
Forms Pellets
Generic Material PVC, Rigid
Generic Name Polyvinyl Chloride, Rigid (PVC, Rigid)
Processing Method Extrusion
PVC Cell Classification 16344
ASTM D1784
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Automotive Applications
Beltline Moldings
General Purpose
Profiles