PolyOne Geon™ HTX Ultra LA426 Tan 3725 Polyvinyl Chloride Alloy (PVC Alloy)

Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ HTX Ultra LA426 Tan 3725 Polyvinyl Chloride Alloy (PVC Alloy).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Optimum for Black and Darker Colors between 50 and 70 L value. Also suitable for colors above 70 L value.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties of Geon HTX Ultra LA426 Tan 3725Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore D 76
76
15 sec; ASTM D2240
Tensile Strength, Yield 38.4 MPa
5570 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 2.04 GPa
296 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 66.9 MPa
9700 psi
ASTM D790
Flexural Modulus 2.09 GPa
303 ksi
ASTM D790
Izod Impact, Notched 6.90 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
12.9 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded; ASTM D256A
Dart Drop Total Energy 59.6 J/cm

@Temperature 23.0 °C
0.112 ft-lb/mil

@Temperature 73.4 °F
Procedure A, C.125; ASTM D4226
178 J/cm

@Temperature 23.0 °C
0.333 ft-lb/mil

@Temperature 73.4 °F
Procedure B, C.125; ASTM D4226
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 91.1 °C

@Thickness 3.18 mm
196 °F

@Thickness 0.125 in
Unannealed; ASTM D648
91.1 °C

@Thickness 3.18 mm
196 °F

@Thickness 0.125 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C

@Thickness 3.18 mm
180 °F

@Thickness 0.125 in
Unannealed; ASTM D648
86.1 °C

@Thickness 3.18 mm
187 °F

@Thickness 0.125 in
Annealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 174 - 193 °C
345 - 379 °F
Descriptive Properties Value Comments
Ease of Sizing Acceptable
Features High Impact Resistance
High Stiffness
Forms Pellets
Generic Material PVC Alloy
Generic Name Polyvinyl Chloride Alloy (PVC Alloy)
Processing Method Extrusion
PVC Cell Classification 15225
ASTM D1784
4-41421-64-0000
ASTM D4216
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Outdoor Applications