PolyOne Geon™ HTX M6307 Polyvinyl Chloride Alloy (PVC Alloy)

Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ HTX M6307 Polyvinyl Chloride Alloy (PVC Alloy).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Spiral Flow 76.2 cm
30.0 in
Mechanical Properties Metric English Comments
Hardness, Shore D 75
75
ASTM D2240
Tensile Strength, Yield 29.6 MPa
4290 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 94 %
94 %
Type I, 51 mm/min; ASTM D638
Tensile Modulus 1.72 GPa
249 ksi
Type I, 51 mm/min; ASTM D638
Flexural Strength 50.3 MPa
7300 psi
ASTM D790
Flexural Modulus 1.79 GPa
260 ksi
ASTM D790
Izod Impact, Notched 1.60 J/cm

@Thickness 3.18 mm,
Temperature -40.0 °C
3.00 ft-lb/in

@Thickness 0.125 in,
Temperature -40.0 °F
Injection Molded; ASTM D256A
3.70 J/cm

@Thickness 3.18 mm,
Temperature -18.0 °C
6.93 ft-lb/in

@Thickness 0.125 in,
Temperature -0.400 °F
Injection Molded; ASTM D256A
5.90 J/cm

@Thickness 3.18 mm,
Temperature 0.000 °C
11.1 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
Injection Molded; ASTM D256A
7.50 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
14.1 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 73.9 °C

@Thickness 6.35 mm
165 °F

@Thickness 0.250 in
Unannealed; ASTM D648
81.1 °C

@Thickness 6.35 mm
178 °F

@Thickness 0.250 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 68.9 °C

@Thickness 6.35 mm
156 °F

@Thickness 0.250 in
Unannealed; ASTM D648
73.9 °C

@Thickness 6.35 mm
165 °F

@Thickness 0.250 in
Annealed; ASTM D648
UL RTI, Electrical 50.0 °C
122 °F
UL 746
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746
Flammability, UL94 V-0

@Thickness 2.01 mm
V-0

@Thickness 0.0791 in
ALL; UL 94
5VA

@Thickness 2.01 mm
5VA

@Thickness 0.0791 in
ALL; UL 94
Processing Properties Metric English Comments
Melt Temperature 202 - 207 °C
396 - 405 °F
Drying Temperature 68.3 °C
155 °F
Dry Time 2.00 hour
2.00 hour
Descriptive Properties Value Comments
Features High Flow
Low Temperature Impact Resistance
Forms Pellets
Generic Material PVC Alloy
Generic Name Polyvinyl Chloride Alloy (PVC Alloy)
Outdoor Suitability f1
UL 746C; Gray
QUV Weatherometer 0.58%
351 Lamp, All Colors, detla E (CIE), 24 hrs light, 300 hrs, No Moisutre
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Construction Applications
Electrical/Electronic Applications
Outdoor Applications
Telecommunications