PolyOne Edgetek® XT XT-115GF-AX01-HF PC+PBT with Glass Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® XT XT-115GF-AX01-HF PC+PBT with Glass Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EDGETEK™ XT High Performance Polymers are polycarbonate and polyester alloys that combine strength, durability and chemical resistance. The Edgetek XT product family includes a complete line of general purpose, UV stable and low-temperature impact grades for use in a wide range of demanding applications and severe operating environments plus customized formulations to meet specialized requirements.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 85.5 MPa
12400 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 4.5 %
4.5 %
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 134 MPa
19400 psi
ASTM D790
Flexural Modulus 4.55 GPa
660 ksi
ASTM D790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.18 mm,
Temperature -20.0 °C
2.00 ft-lb/in

@Thickness 0.125 in,
Temperature -4.00 °F
Injection Molded; ASTM D256A
1.44 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
2.70 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 113 °C

@Thickness 6.35 mm
235 °F

@Thickness 0.250 in
Annealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 260 - 282 °C
500 - 540 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 110 °C

@Time 7200 sec
230 °F

@Time 2.00 hour
Descriptive Properties Value Comments
Features High Flow
Forms Pellets
Generic Name Polycarbonate + PBT (PC+PBT)
Regional Availability Africa & Middle East