PolyOne Edgetek® X TR2-20TA/000 NATURAL Copolyester

Category Polymer , Thermoplastic , Polyester, TP
Manufacturer PolyOne Corporation
Trade Name Edgetek®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® X TR2-20TA/000 NATURAL Copolyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Edgetek™ engineering thermoplastics compounds made with Eastman Tritan™ copolyester offer a wide range of performance and properties with the addition of reinforcing additives. By utilizing Eastman Tritan™ copolyester these compounds provide chemical resistance, clarity, heat resistance and BPA-free solutions.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0030 cm/cm

@Thickness 3.18 mm
0.0020 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.7 MPa
5900 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield 51.7 MPa
7500 psi
5.1 mm/min; ASTM D638
Elongation at Break 30 %
30 %
Type I, 5.1 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
5.1 mm/min; ASTM D638
Tensile Modulus 3.38 GPa
490 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 89.6 MPa
13000 psi
1.3 mm/min; ASTM D790
Flexural Modulus 3.03 GPa
439 ksi
1.3 mm/min; ASTM D790
Izod Impact, Notched 0.750 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
1.41 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Izod Impact, Unnotched 21.0 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
39.3 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded, Partial Break; ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature -30.0 - 30.0 °C
61.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM E831
CTE, linear, Transverse to Flow 140 µm/m-°C

@Temperature -30.0 - 30.0 °C
77.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 112 °C

@Thickness 3.18 mm
234 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 103 °C

@Thickness 3.18 mm
217 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 266 - 282 °C
511 - 540 °F
Mold Temperature 60.0 - 65.6 °C
140 - 150 °F
Drying Temperature 87.8 °C
190 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Features BPA Free
Crazing Resistant
Filled
Good Chemical Resistance
Good Crack Resistance
Good Dimensional Stability
Good Toughness
Medium Clarity
Medium Heat Resistance
Filler / Reinforcement Mineral Filler
Forms Pellets
Generic Material Copolyester
Generic Name Copolyester
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Appliance Components
Consumer Applications
Food Service Applications
Household Goods
Industrial Applications