PolyOne Edgetek® X TR2-10TA/000 NATURAL Copolyester
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® X TR2-10TA/000 NATURAL Copolyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Edgetek™ engineering thermoplastics compounds made with Eastman Tritan™ copolyester offer a wide range of performance and properties with the addition of reinforcing additives. By utilizing Eastman Tritan™ copolyester these compounds provide chemical resistance, clarity, heat resistance and BPA-free solutions.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.18 mm |
0.0030 - 0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.7 MPa | 5900 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | 5.1 mm/min; ASTM D638 |
| Elongation at Break | 58 % | 58 % | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.28 GPa | 331 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded, Method A; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
| CTE, linear, Transverse to Flow | 170 µm/m-°C @Temperature -30.0 - 30.0 °C |
94.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 3.18 mm |
232 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 3.18 mm |
212 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 266 - 282 °C | 511 - 540 °F | |
| Mold Temperature | 60.0 - 65.6 °C | 140 - 150 °F | |
| Drying Temperature | 87.8 °C | 190 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | BPA Free | |
| Crazing Resistant | ||
| Filled | ||
| Good Chemical Resistance | ||
| Good Crack Resistance | ||
| Good Dimensional Stability | ||
| Good Toughness | ||
| Medium Clarity | ||
| Medium Heat Resistance | ||
| Filler / Reinforcement | Mineral Filler | |
| Forms | Pellets | |
| Generic Material | Copolyester | |
| Generic Name | Copolyester | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Unnotched Izod Impact | No Break | ASTM D256; 23°C, 3.18 mm, Injection Molded |
| Uses | Appliance Components | |
| Consumer Applications | ||
| Food Service Applications | ||
| Household Goods | ||
| Industrial Applications | ||
| Transparent or Translucent Parts |