PolyOne Edgetek® UR-30GF/000 Thermoplastic Elastomer - TPU, Glass Filled  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® UR-30GF/000 Thermoplastic Elastomer - TPU, Glass Filled  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description/Features:Glass Fiber ReinforcedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D792
Water Absorption 0.25 %
0.25 %
24 hr. Immersion; ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 51.7 MPa
7500 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
Elongation at Break 15 %
15 %
Type 1 - Rigids, 0.2 in/min; ASTM D638
Tensile Modulus 1.52 GPa
220 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
Flexural Strength 55.2 MPa
8000 psi
ASTM D790
Flexural Modulus 1.38 GPa
200 ksi
ASTM D790
Izod Impact, Notched 4.81 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
9.00 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
Method A, Injection Molded; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 104 °C
220 °F
Annealed, 0.125 in bars; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Annealed, 0.125 in bars; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 193 - 216 °C
380 - 420 °F
Molding
Mold Temperature 15.6 - 37.8 °C
60.0 - 100 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 2 hour
2 hour
Descriptive Properties Value Comments
Product Form Pellets
Rockwell Hardness 65 D
ASTM D785