PolyOne Edgetek® PC-15CF/000 FCR Polycarbonate (PC)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer PolyOne Corporation
Trade Name Edgetek®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® PC-15CF/000 FCR Polycarbonate (PC).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Edgetek™ Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Water Absorption 0.15 %
0.15 %
@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16500 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 3.0 %
3.0 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 6.89 GPa
999 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 172 MPa
24900 psi
ASTM D790
Flexural Modulus 6.89 GPa
999 ksi
ASTM D790
Izod Impact, Notched 0.800 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
1.50 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C
7.78 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 149 °C

@Thickness 3.18 mm
300 °F

@Thickness 0.125 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 143 °C

@Thickness 3.18 mm
289 °F

@Thickness 0.125 in
Annealed; ASTM D648
Flammability, UL94 HB
HB
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 100 ohm-cm - 1e+05
100 ohm-cm - 1e+05
ASTM D257
Surface Resistance 100 ohm - 1e+05
100 ohm - 1e+05
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 288 - 321 °C
550 - 610 °F
Mold Temperature 82.2 - 107 °C
180 - 225 °F
Drying Temperature 121 °C
250 °F
Dry Time 2.00 hour
2.00 hour
Descriptive Properties Value Comments
Features Fast Molding Cycle
Filler / Reinforcement Carbon Fiber Reinforcement, 15% Filler by Weight
Forms Pellets
Generic Material PC
Generic Name Polycarbonate (PC)
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant