PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.24 % @Thickness 3.17 mm |
0.24 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Water Absorption at Saturation | 2.2 % @Thickness 3.17 mm |
2.2 % @Thickness 0.125 in |
Long-Term Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 179 MPa | 26000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- LG Chemical HI855M PMMA, Impact Resistant Grade
- LG Chemical LUCEL FW-710F Friction and Wear Resistant POM, PTEE filled
- Momentive Performance Materials Siloprenâ„¢ LSR 2345/05 Electrically-Conductive Liquid Silicone Rubber
- Karina E 808-47/14-IS-RG Silver PVC Compound
- Skamol Group SKAMOLEX V-1100 (700) Customized Shape
- Teknor Apex Fireguard® 910L16-C6-NL1 Polyvinyl Chloride, Flexible
- Ensinger Tecapeek® XP-90 Compression Molded PEEK Compound, 25% Fiberglass
- BNZ Materials BNZ-23 Insulating Firebrick
- Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (8 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved