PolyOne Edgetek® NI-30CF/000 Nylon 6/10 - 30% Carbon Fiber Reinforced  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® NI-30CF/000 Nylon 6/10 - 30% Carbon Fiber Reinforced  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ASTM D792
Water Absorption 0.20 %
0.20 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.17 mm
 0.0020 - 0.0030 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 193 MPa
28000 psi
ASTM D638
Elongation at Break 3.0 - 4.0 %
3.0 - 4.0 %
ASTM D638
Flexural Yield Strength 276 MPa
40000 psi
ASTM D790
Flexural Modulus 13.8 GPa
2000 ksi
ASTM D790
Izod Impact, Notched 1.33 J/cm

@Thickness 6.35 mm
 2.49 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear 16.2 µm/m-°C

@Temperature 20.0 °C
 9.00 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 218 °C
424 °F
ASTM D648
Electrical Properties Metric English Comments
Electrical Resistivity 100 ohm-cm
100 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 271 - 293 °C
520 - 559 °F
Stock
Mold Temperature 82.0 - 107 °C
180 - 225 °F
Drying Temperature 82.0 °C
180 °F