PolyOne Edgetek® BB-20GF/000 PC/ABS Blend, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® BB-20GF/000 PC/ABS Blend, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.291 g/cc | 1.291 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0025 cm/cm | 0.0020 - 0.0025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.21 GPa | 900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 271 °C | 450 - 520 °F | Molding |
| Mold Temperature | >= 93.3 °C | >= 200 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- LATI LATILUB 88/50-30GRT PEEK Based, 30% Graphite and PTFE Self Lubricating Plastic (Unverified Data**)&l
- Huntsman AroCy B-10 Monomeric Bisphenol-A Dicyanate
- Mitsubishi Iupilon® S3000UR 16.5 MFI, UV Stabilized Polycarbonate With Release
- Lucite International Colacryl ® D150 Acrylic Dental Resin
- Chase Plastics CP Pryme® NN143GL (COND, 50% RH) Nylon 66, 43% Glass Fiber Reinforced, Internally Lubricated
- A. Schulman SCHULAMID® 6 NV12 Easy Flow Low Viscosity Nylon 6
- Hexcel® HexWeb® HRP/F35 - 2.5 Nonmetallic Flex-Core Honeycomb
- Trimay® Wear Plate TWP170 Flux Cored Weld Wire & Electrode
- 3M 7741 Polyester Overlaminating Film
Copyright © lookpolymers.com All Rights Reserved