PolyOne Edgetek® AT-000/000 HI5 Natural NA Acetal (POM) Copolymer

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	PolyOne Corporation
Trade Name	Edgetek®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Edgetek® AT-000/000 HI5 Natural NA Acetal (POM) Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.38 g/cc	1.38 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.020 cm/cm	0.020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	48.3 MPa	7010 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	>= 10 %	>= 10 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	2.07 GPa	300 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	68.9 MPa	9990 psi	ASTM D790
Flexural Modulus	2.07 GPa	300 ksi	ASTM D790
Izod Impact, Notched	1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Processing Properties	Metric	English	Comments
Melt Temperature	188 - 210 °C	370 - 410 °F

Descriptive Properties	Value	Comments
Features	Copolymer
	Impact Modified
Forms	Pellets
Generic Material	Acetal (POM) Copolymer
Generic Name	Acetal (POM) Copolymer
Processing Method	Injection Molding
Regional Availability	North America
Uses	Automotive Applications
	Consumer Applications
	Industrial Applications