- PolyOne Edgetek® AM-40CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced (discontinued **)
PolyOne Edgetek® AM-40CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AM-40CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Thickness 3.17 mm |
0.10 % @Thickness 0.125 in |
24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 207 MPa | 30000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 28.3 GPa | 4100 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 352 MPa | 51000 psi | ASTM D790 |
| Flexural Modulus | 24.1 GPa | 3500 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 316 °C | 600 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding |
Users viewing this material also viewed the following:
- Ovation Polymers UTTAP QU HT530 GF Nylon, 30% Glass Reinforced
- Nilit Polynil® P50L Externally Lubricated Nylon 66
- Arlon Silicone Hose and Duct Material with Polyester Substrate (65390R042) (discontinued **)
- 3M Dyneon™ CC155 Custom Fluoropolymer Compound (discontinued **)
- SABIC Innovative Plastics LNP STAT-KON RE0039 PA 66
- Universal Wire Works BAu-5 (AMS 4785) Gold Brazing Filler Metal
- A. Schulman PP 3479-01 Polypropylene Random Copolymer
- Loctite® 3445 1 component fusible solder filler Anisotropic Epoxy Adhesive
- Eurostar Starpylen MF003SU PP, 15% Glass Fiber Filled, Injection Molded
- Grupo Repol Dinalon® B2S35 V2-7035 PA6 High Viscosity, V2 Halogen Free, RAL 7035
Copyright © lookpolymers.com All Rights Reserved