PolyOne Edgetek® AM-35GF/000 FR NH Polyphthalamide (PPA)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer PolyOne Corporation
Trade Name Edgetek®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® AM-35GF/000 FR NH Polyphthalamide (PPA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
ISO 1183
Maximum Moisture Content <= 0.10
<= 0.10
Linear Mold Shrinkage 0.0010 cm/cm

@Thickness 2.00 mm
 0.0010 in/in

@Thickness 0.0787 in
 Flow; ISO 294-4
0.0070 cm/cm

@Thickness 2.00 mm
 0.0070 in/in

@Thickness 0.0787 in
 Across Flow; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-2
Elongation at Break 2.0 %
2.0 %
ISO 527-2
Tensile Modulus 12.5 GPa
1810 ksi
ISO 527-2
Flexural Strength 210 MPa
30500 psi
ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 320 - 330 °C
608 - 626 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Annealed; ISO 75-2/A
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 UL 94
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 UL 94
V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 UL 94
Oxygen Index >= 34 %
>= 34 %
ISO 4589-2
Glow Wire Test 750 °C

@Thickness 1.60 mm
 1380 °F

@Thickness 0.0630 in
 Ignition Temperature; IEC 60695-2-13
750 °C

@Thickness 0.800 mm
 1380 °F

@Thickness 0.0315 in
 Ignition Temperature; IEC 60695-2-13
775 °C

@Thickness 3.00 mm
 1430 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 320 - 340 °C
608 - 644 °F
Mold Temperature 90.0 - 120 °C
194 - 248 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Features Flame Retardant
Halogen Free
Filler / Reinforcement Glass Fiber Reinforcement, 35% Filler by Weight
Forms Pellets
Generic Material PPA
Generic Name Polyphthalamide (PPA)
Processing Method Injection Molding
Regional Availability Europe
Uses Automotive Applications
Electrical/Electronic Applications
General Purpose
Industrial Applications