PolyOne Edgetek® AM-20CF-20GF/000 Polyphthalamide (PPA), Glass/Carbon Fiber Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AM-20CF-20GF/000 Polyphthalamide (PPA), Glass/Carbon Fiber Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass/Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.423 g/cc | 1.423 g/cc | ASTM D792 |
| Water Absorption | 0.17 % | 0.17 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 207 MPa | 30000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 17.2 GPa | 2500 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 259 MPa | 37500 psi | ASTM D790 |
| Flexural Modulus | 17.2 GPa | 2500 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 299 °C | 570 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 293 °C | 560 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding |
| Mold Temperature | >= 135 °C | >= 275 °F | |
| Drying Temperature | 110 - 121 °C | 230 - 250 °F | |
| Dry Time | 6 hour | 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S KG 60A-3S2018 Thermoplastic Elastomer (TPE)
- 3M Dyneon™ TF 4212 PTFE 10% Electrocarbon Filled (discontinued **)
- Haynes Hastelloy® N, weld metal as welded
- SABIC Innovative Plastics LNP THERMOCOMP OC006 PPS - Linear (Asia Pacific)
- Chosun Refractories INCT-100N Light-Weight Castable
- Colorite Polymers 10013G-015 (Molding) Radiation Sterilizable Vinyl Compound
- Arlon 55606R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Scotch-Weld™ TL71 Threadlocker Anaerobic Adhesive
- DuPont Performance Polymers Zytel® SC315 NC010 Nylon 612 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved