PolyOne Edgetek® 5230 Natural 1 Acetal (POM) Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® 5230 Natural 1 Acetal (POM) Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Thickness 3.18 mm |
0.20 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.025 - 0.027 cm/cm | 0.025 - 0.027 in/in | ASTM D955 |
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 64.1 MPa | 9300 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.34 GPa | 339 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 3.18 mm |
230 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Copolymer | |
| General Purpose | ||
| Good Wear Resistance | ||
| High Flow | ||
| Low Friction | ||
| Forms | Pellets | |
| Generic Material | Acetal (POM) Copolymer | |
| Generic Name | Acetal (POM) Copolymer | |
| Processing Method | Injection Molding | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Automotive Applications | |
| Bearings | ||
| Business Equipment | ||
| Consumer Applications | ||
| Gears | ||
| General Purpose | ||
| Industrial Applications | ||
| Pulleys | ||
| Rollers |