PolyOne Dynaflex™ G7650-9 (Black) Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Dynaflex™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Dynaflex™ G7650-9 (Black) Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Dynaflex™ G7650-9 (Black) is an easy processing, general purpose TPE designed for a wide variety of applications, including those where FDA compliance is required. - Overmold Adhesion to Polypropylene - Rubbery Feel - Soft TouchPurge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Regrind levels up to 20% can be used with Dynaflex™ G7650-9 (Black) with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Dynaflex™ G7650-9 (Black) has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer. Drying is not Required Injection Speed: 1 to 5 in/sec 1st Stage - Boost Pressure: 350 to 750 psi 2nd Stage - Hold Pressure: 50% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
Viscosity 9100 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
9100 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
46800 cP

@Shear Rate 1340 1/s,
Temperature 200 °C
46800 cP

@Shear Rate 1340 1/s,
Temperature 392 °F
ASTM D3835
Linear Mold Shrinkage, Flow 0.011 - 0.019 cm/cm
0.011 - 0.019 in/in
ASTM D955
Melt Flow 9.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
9.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 48
48
10 sec; ASTM D2240
Tensile Strength at Break 4.83 MPa

@Temperature 23.0 °C
701 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 1.52 MPa

@Strain 100 %,
Temperature 23.0 °C
220 psi

@Strain 100 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
2.76 MPa

@Strain 300 %,
Temperature 23.0 °C
400 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 700 %

@Temperature 23.0 °C
700 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tear Strength 20.5 kN/m
117 pli
ASTM D624
Compression Set 12 %

@Temperature 23.0 °C,
Time 79200 sec
12 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395B
Processing Properties Metric English Comments
Rear Barrel Temperature 160 - 177 °C
320 - 351 °F
Middle Barrel Temperature 177 - 188 °C
351 - 370 °F
Front Barrel Temperature 188 - 216 °C
370 - 421 °F
Nozzle Temperature 188 - 227 °C
370 - 441 °F
Mold Temperature 15.6 - 26.7 °C
60.1 - 80.1 °F
Back Pressure 0.000 - 1.03 MPa
0.000 - 149 psi
Screw Speed 40 - 100 rpm
40 - 100 rpm
Descriptive Properties Value Comments
Agency Ratings FDA 21 CFR 177.1210
Please contact GLS Thermoplastic Elastomers for a copy of the FDA compliance letter.
Appearance Black
Features General Purpose
Good Flow
Good Processability
Good Processing Stability
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Extrusion
Injection Molding
Regional Availability Asia Pacific
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%
Uses Consumer Applications
Flexible Grips
Gaskets
General Purpose
Overmolding
Seals
Soft Touch Applications