PolyOne Bergamid™ A700 G20 HW UF Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name Bergamid™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Bergamid™ A700 G20 HW UF Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
±0.03 g/cm³; DIN 53479
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa

@Temperature 23.0 °C
 16700 psi

@Temperature 73.4 °F
 ISO 527-2/5
Elongation at Break 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
 ISO 527-2/5
Tensile Modulus 8.00 GPa

@Temperature 23.0 °C
 1160 ksi

@Temperature 73.4 °F
 ISO 527-2/1
Charpy Impact Unnotched 4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²

@Temperature 23.0 °C
 2.62 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 261 °C
502 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
Unannealed; ISO 75-2/A
Vicat Softening Point 245 °C
473 °F
ISO 306/A50
245 °C
473 °F
ISO 306/B50
UL RTI, Electrical 125 °C

@Thickness 0.750 mm
 257 °F

@Thickness 0.0295 in
 UL 746
125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
 UL 746
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 100 °C

@Thickness 0.750 mm
 212 °F

@Thickness 0.0295 in
 UL 746
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 UL 746
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 105 °C

@Thickness 0.750 mm
 221 °F

@Thickness 0.0295 in
 UL 746
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
 UL 746
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 ALL; UL 94
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
 ALL; UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 ALL; UL 94
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 ALL; UL 94
Glow Wire Test 725 °C

@Thickness 0.800 mm
 1340 °F

@Thickness 0.0315 in
 Ignition Temperature; IEC 60695-2-13
725 °C

@Thickness 1.60 mm
 1340 °F

@Thickness 0.0630 in
 Ignition Temperature; IEC 60695-2-13
750 °C

@Thickness 3.00 mm
 1380 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 0.400 mm
 1760 °F

@Thickness 0.0157 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Hold Pressure 40.0 - 90.0 MPa
5800 - 13100 psi
Descriptive Properties Value Comments
Comparative Tracking Index (CTI) PLC 1
UL 746
Features Flame Retardant
Halogen Free
Heat Stabilized
Hydrolysis Resistant
Filler / Reinforcement Glass Fiber Reinforcement, 20% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Outdoor Suitability f1
UL 746C; Black
Processing Method Extrusion
Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
RoHS Compliance RoHS Compliant
UL File Number E76261