PolyOne Bergamid™ A700 G15 HW UF Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name Bergamid™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Bergamid™ A700 G15 HW UF Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
These products contain flame retardants which are activated by longer residence times in the cylinder and then can decompose. At interruption of the moulding cycle (approx. >5 min) it is recommended to jet melt completely and to clean the cylinder, e.g. with a standard polyamide.Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
±0.03 g/cm³; DIN 53479
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa

@Temperature 23.0 °C
 15200 psi

@Temperature 73.4 °F
 ISO 527-2/5
Elongation at Break 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
 ISO 527-2/5
Tensile Modulus 7.00 GPa

@Temperature 23.0 °C
 1020 ksi

@Temperature 73.4 °F
 ISO 527-2/1
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 261 °C
502 °F
ISO 3146
UL RTI, Electrical 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 UL 746
125 °C

@Thickness 0.750 mm
 257 °F

@Thickness 0.0295 in
 UL 746
125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
 UL 746
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 UL 746
100 °C

@Thickness 0.750 mm
 212 °F

@Thickness 0.0295 in
 UL 746
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 UL 746
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 UL 746
105 °C

@Thickness 0.750 mm
 221 °F

@Thickness 0.0295 in
 UL 746
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
 UL 746
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 ALL; UL 94
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
 ALL; UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 ALL; Internal Method
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 ALL; UL 94
Glow Wire Test 960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 °C
176 °F
Desiccant Dryer
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Desiccant Dryer
Hold Pressure 40.0 - 90.0 MPa
5800 - 13100 psi
Descriptive Properties Value Comments
Additive Heat Stabilizer
Comparative Tracking Index (CTI) PLC 0
UL 746; 3.00 mm
Features Flame Retardant
Halogen Free
Heat Stabilized
Filler / Reinforcement Glass Fiber Reinforcement, 15% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
RoHS Compliance RoHS Compliant
UL File Number E76261