Polimeri Europa Sinkral® D 232/M3 ABS Resin  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Sinkral® D 232/M3 ABS Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Special low gloss extrusion/ co-extrusion grade, with good flow. Designation: Thermoplastic ISO 2580-ABS 1, EGN, 105-08-09-15Applications: Sinkral D 232-M3 is widely used in the extrusion / co-extrusion of foils, when a very high matt appearance is required, as well as in the extrusion of profiles.This grade is supplied in natural only for self-coloring. Sinkral D 232/M3 meets European Standards for plastics in contact with foods.Information provided by Polimeri EuropaISO 2580-ABS 1, EGN, 105-08-09-15
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
24 hours - 23°C; ASTM D 570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Melt Flow 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 97
97
ISO 2039/2
Tensile Strength, Yield 27.0 MPa
3920 psi
50 mm/min; ASTM D 638
Elongation at Break 100 %
100 %
50 mm/min; ASTM D 638
Flexural Strength 40.0 MPa
5800 psi
2 mm/min; ASTM D 790
Flexural Modulus 1.55 GPa
225 ksi
2 mm/min; ASTM D 790
Izod Impact, Notched 0.750 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
1.41 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
ISO 180/4A
0.800 J/cm

@Thickness 3.20 mm,
Temperature -20.0 °C
1.50 ft-lb/in

@Thickness 0.126 in,
Temperature -4.00 °F
ISO 180/4A
0.900 J/cm

@Thickness 3.20 mm,
Temperature 0.000 °C
1.69 ft-lb/in

@Thickness 0.126 in,
Temperature 32.0 °F
ISO 180/4A
1.10 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.06 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ISO 180/4A
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Thickness 4.00 mm,
Temperature -40.0 °C
3.33 ft-lb/in²

@Thickness 0.157 in,
Temperature -40.0 °F
ISO 180/1A
9.50 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
4.52 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
DIN 53453
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
DIN 53453
Charpy Impact, Notched 0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
DIN 53453
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
ASTM C 177
Deflection Temperature at 1.8 MPa (264 psi) 101 °C
214 °F
120°C/h; ASTM D 648
Vicat Softening Point 101 °C
214 °F
50 N - 120°C/h; ISO 306/B120
106 °C
223 °F
10 N - 120°C/h; ISO 306/A120
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Glow Wire Test 650 °C

@Thickness 3.00 mm
1200 °F

@Thickness 0.118 in
IEC 60695-2-1
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Dry; IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dry; IEC 60093
Dielectric Constant 3.1

@Frequency 1000 Hz
3.1

@Frequency 1000 Hz
Dry; IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
Dry; IEC 60243
Dissipation Factor 0.015

@Frequency 1000 Hz
0.015

@Frequency 1000 Hz
dry; IEC 60250
Processing Properties Metric English Comments
Melt Temperature 180 - 220 °C
356 - 428 °F
Drying Temperature 80.0 °C
176 °F
No venting in an air circulating oven
Dry Time 2 - 4 hour
2 - 4 hour
No venting in an air circulating oven