Polimeri Europa Sinkral® C 442 ABS Resin

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Sinkral®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Sinkral® C 442 ABS Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sinkral C 442 is a heat resistant injection molding grade offering good flow and impact resistance together with excellent thermal stability during processing. Designation: Thermoplastic ISO 2580-ABS 1,MGN,105-08-16-20Applications: Thanks to a low Yellow Index and color constancy, it is suitable for self-coloring, mainly in the automotive industry for interior (extruded profiles, interior trim,..) and with proper masterbatches, for exterior parts such as grilles and rear view mirrors.Grade available either in natural or colored versions. Suitable masterbatches could be recommended for self-coloring.Information provided by Polimeri EuropaISO 2580-ABS 1, MGN, 105-08-16-20
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
24 hours - 23°C; ASTM D 570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Melt Flow 6.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
6.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ISO 2039/2
Tensile Strength, Yield 43.0 MPa
6240 psi
50 mm/min; ASTM D 638
Elongation at Break 45 %
45 %
50 mm/min; ASTM D 638
Flexural Strength 65.0 MPa
9430 psi
2 mm/min; ASTM D 790
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ASTM D 790
Izod Impact, Notched 1.00 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
1.87 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
ISO 180/4A
1.25 J/cm

@Thickness 3.20 mm,
Temperature -20.0 °C
2.34 ft-lb/in

@Thickness 0.126 in,
Temperature -4.00 °F
ISO 180/4A
1.65 J/cm

@Thickness 3.20 mm,
Temperature 0.000 °C
3.09 ft-lb/in

@Thickness 0.126 in,
Temperature 32.0 °F
ISO 180/4A
2.00 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
3.75 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ISO 180/4A
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Thickness 4.00 mm,
Temperature -40.0 °C
4.28 ft-lb/in²

@Thickness 0.157 in,
Temperature -40.0 °F
ISO 180/1A
17.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
8.09 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
DIN 53453
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
DIN 53453
Charpy Impact, Notched 1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
DIN 53453
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
ASTM C 177
Deflection Temperature at 1.8 MPa (264 psi) 108 °C
226 °F
120°C/h; ASTM D 648
Vicat Softening Point 108 °C
226 °F
50 N - 120°C/h; ISO 306/B120
114 °C
237 °F
10 N - 120°C/h; ISO 306/A120
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Glow Wire Test 650 °C

@Thickness 3.00 mm
1200 °F

@Thickness 0.118 in
IEC 60695-2-1
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Dry; IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dry; IEC 60093
Dielectric Constant 3.1

@Frequency 1000 Hz
3.1

@Frequency 1000 Hz
Dry; IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
Dry; IEC 60243
Dissipation Factor 0.015

@Frequency 1000 Hz
0.015

@Frequency 1000 Hz
dry; IEC 60250
Processing Properties Metric English Comments
Melt Temperature 230 - 270 °C
446 - 518 °F
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Drying Temperature 80.0 °C
176 °F
No venting in an air circulating oven
Dry Time 2 - 4 hour
2 - 4 hour
No venting in an air circulating oven