Polimeri Europa Sinkral® B 432/E ABS Resin

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Sinkral®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Sinkral® B 432/E ABS Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sinkral B 432/E is a general purpose extrusion grade which exhibits a good balance between rigidity and toughness. Designation: Thermoplastic ISO 2580-ABS 1,EGN,105-04-16-20Applications: Large sheets with good surface finish (co-extruded or not and with high draw ratios) for a variety of uses in sectors such as refrigeration, sanitary, automotive, packaging and furnitures (profiles).Grade available in natural color only. Suitable masterbatches could be recommended for self-coloring. The composition of this grade meets European Regulations for packaging in contact with foodstuffs.Information provided by Polimeri EuropaISO 2580-ABS 1, EGN, 105-04-16-20
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
24 hours - 23°C; ASTM D 570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Melt Flow 4.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
4.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ISO 2039/2
Tensile Strength, Yield 45.0 MPa
6530 psi
50 mm/min; ASTM D 638
Elongation at Break 45 %
45 %
50 mm/min; ASTM D 638
Flexural Strength 68.0 MPa
9860 psi
2 mm/min; ASTM D 790
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ASTM D 790
Izod Impact, Notched 1.00 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
1.87 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
ISO 180/4A
1.25 J/cm

@Thickness 3.20 mm,
Temperature -20.0 °C
2.34 ft-lb/in

@Thickness 0.126 in,
Temperature -4.00 °F
ISO 180/4A
1.65 J/cm

@Thickness 3.20 mm,
Temperature 0.000 °C
3.09 ft-lb/in

@Thickness 0.126 in,
Temperature 32.0 °F
ISO 180/4A
2.20 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
4.12 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ISO 180/4A
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Thickness 4.00 mm,
Temperature -40.0 °C
4.28 ft-lb/in²

@Thickness 0.157 in,
Temperature -40.0 °F
ISO 180/1A
17.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
8.09 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
DIN 53453
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
DIN 53453
Charpy Impact, Notched 1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
DIN 53453
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
ASTM C 177
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
219 °F
120°C/h; ASTM D 648
Vicat Softening Point 104 °C
219 °F
50 N - 120°C/h; ISO 306/B120
109 °C
228 °F
10 N - 120°C/h; ISO 306/A120
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Glow Wire Test 650 °C

@Thickness 3.00 mm
1200 °F

@Thickness 0.118 in
IEC 60695-2-1
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Dry; IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dry; IEC 60093
Dielectric Constant 3.1

@Frequency 1000 Hz
3.1

@Frequency 1000 Hz
Dry; IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
Dry; IEC 60243
Dissipation Factor 0.015

@Frequency 1000 Hz
0.015

@Frequency 1000 Hz
dry; IEC 60250
Processing Properties Metric English Comments
Melt Temperature 190 - 230 °C
374 - 446 °F
Drying Temperature 80.0 °C
176 °F
No venting in an air circulating oven
Dry Time 2 - 4 hour
2 - 4 hour
No venting in an air circulating oven