Polimeri Europa SINKRAL PD H210/K ABS  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa SINKRAL PD H210/K ABS  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,085-25-16-25 Flame retarded (PBBE free) injection moulding grade, rated UL94-5V at 3.2 mm thick and UL 94V-0 at 1.6 mm thick. This material presents a good fluidity, a good impact resistance and also a good UV resistance. Applications: computer housings, electrical appliances, business machines.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Water Absorption 1.0 %
1.0 %
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Humidity Absorption
Melt Flow 15.5 g/10 min

@Load 10.0 kg,
Temperature 220 °C
15.5 g/10 min

@Load 22.0 lb,
Temperature 428 °F
cm³/10 min
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.0 MPa
5220 psi
50 mm/min
Elongation at Break 20 %
20 %
Nominal
Elongation at Yield 2.6 %
2.6 %
50 mm/min
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min
Charpy Impact Unnotched 9.00 J/cm²
42.8 ft-lb/in²
5.00 J/cm²

@Temperature -30.0 °C
23.8 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 84.0 °C
183 °F
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
Vicat Softening Point 87.0 °C
189 °F
50°C/hr; 50N
Glass Transition Temp, Tg 106 °C
223 °F
10°C/min test
Flammability, UL94 V-0

@Thickness 1.57 mm
V-0

@Thickness 0.0618 in
V-0

@Thickness 3.17 mm
V-0

@Thickness 0.125 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Strength 32.0 kV/mm
813 kV/in
Comparative Tracking Index 500 V
500 V