- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Polimeri Europa SINKRAL PD G523 ABS, Impact Grade (discontinued **)
Polimeri Europa SINKRAL PD G523 ABS, Impact Grade (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa SINKRAL PD G523 ABS, Impact Grade
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-15-25-20 High impact injection moulding grade. Other characteristics: good flow, excellent thermal stability during processing and easily painted. SINKRAL PD G523 is particularly suitable for large and complex parts subjected to high mechanical stress in automotive interiors. Also used in the production of fairings and paintable bodies of scooters and mopeds.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Water Absorption | 1.0 % | 1.0 % | |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Humidity Absorption |
| Melt Flow | 18 g/10 min @Load 10.0 kg, Temperature 220 °C |
18 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 50 mm/min |
| Elongation at Break | 35 % | 35 % | Nominal |
| Elongation at Yield | 2.8 % | 2.8 % | 50 mm/min |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| 18.0 J/cm² @Temperature -30.0 °C |
85.7 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | |
| Vicat Softening Point | 97.0 °C | 207 °F | 50°C/hr; 50N |
| Glass Transition Temp, Tg | 108 °C | 226 °F | 10°C/min test |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | |
| Comparative Tracking Index | 600 V | 600 V |