Polimeri Europa SINKRAL PD G120 ABS  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa SINKRAL PD G120 ABS  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-15-09-30 General purpose injection moulding grade. Characteristics: outstanding rigidity very high surface hardness high gloss good flow SINKRAL G120 is particularly recommended for applications in home furnishing, video & photographic equipment and air conditioning equipment. Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Water Absorption 1.0 %
1.0 %
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Humidity Absorption
Melt Flow 17 g/10 min

@Load 10.0 kg,
Temperature 220 °C
17 g/10 min

@Load 22.0 lb,
Temperature 428 °F
cm³/10 min
Mechanical Properties Metric English Comments
Tensile Strength, Yield 52.0 MPa
7540 psi
50 mm/min
Elongation at Break 10 %
10 %
Nominal
Elongation at Yield 3.0 %
3.0 %
50 mm/min
Tensile Modulus 2.80 GPa
406 ksi
1 mm/min
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C
205 °F
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
Vicat Softening Point 99.0 °C
210 °F
50°C/hr; 50N
Glass Transition Temp, Tg 108 °C
226 °F
10°C/min test
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Strength 30.0 kV/mm
762 kV/in
Comparative Tracking Index 600 V
600 V
Users viewing this material also viewed the following: