Polimeri Europa SINKRAL L320 ABS  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa SINKRAL L320 ABS  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-25-16-25 General purpose, high flow injection moulding grade having good impact resistance coupled with an excellent gloss. Normally used in the small appliance industry, as well as for vacuum cleaners, toys, telephones and consumer electronics.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data except as noted. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Water Absorption 1.0 %
1.0 %
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Humidity Absorption
Melt Flow 5.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
5.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
Cond. I; ASTM D1238
22 g/10 min

@Load 10.0 kg,
Temperature 220 °C
22 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ASTM D785
Tensile Strength, Yield 43.0 MPa
6240 psi
50 mm/min
Elongation at Break 10 %
10 %
Nominal
Elongation at Yield 3.2 %
3.2 %
50 mm/min
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min
Flexural Modulus 2.48 GPa
360 ksi
ASTM D790
Izod Impact, Notched 2.90 J/cm

@Thickness 3.17 mm
5.43 ft-lb/in

@Thickness 0.125 in
ASTM D256
Charpy Impact Unnotched 17.0 J/cm²
80.9 ft-lb/in²
11.0 J/cm²

@Temperature -30.0 °C
52.4 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C
198 °F
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Vicat Softening Point 97.0 °C
207 °F
50°C/hr; 50N
Glass Transition Temp, Tg 105 °C
221 °F
10°C/min test
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Strength 30.0 kV/mm
762 kV/in
Comparative Tracking Index 600 V
600 V