Polimeri Europa Riblene® FM 23 Low Density Polyethylene - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Riblene® FM 23 Low Density Polyethylene - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Riblene FM 23 is a low density polyethylene (LDPE) with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FM 23 is characterized by a good balance between processability, mechanical, and optical properties.Films manufactured with Riblene FM 23 are easily heat shrinkable.Main Applications: Riblene FM 23 is recommended for general packaging film, for the production of thin transparent film and for blend.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.921 g/cc
0.921 g/cc
ISO 1183
Thickness 18.0 - 50.0 microns
0.709 - 1.97 mil
Recommended
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ISO 527-3
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ISO 527-3
Film Elongation at Break, MD 300 %
300 %
ISO 527-3
Film Elongation at Break, TD 550 %
550 %
ISO 527-3
Coefficient of Friction, Dynamic 0.10
0.10
ISO 8295
Elmendorf Tear Strength, MD 6.114 g/micron
155.3 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 4.076 g/micron
103.5 g/mil
ISO 6383-2
Dart Drop Test 150 g
0.331 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ISO 527-3
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ISO 527-3
1% Secant Modulus, MD 160 MPa
23200 psi
ISO 527-3
1% Secant Modulus, TD 170 MPa
24700 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 111 °C
232 °F
Internal method
Vicat Softening Point 90.0 °C

@Load 1.00 kg
194 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746
Optical Properties Metric English Comments
Haze 6.5 %
6.5 %
ISO 14782
Gloss 68 %
68 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
transparent; thickness not quantified