Polimeri Europa Riblene® FL 30 Low Density Polyethylene - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Riblene® FL 30 Low Density Polyethylene - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Riblene FL 30 is a low density polyethylene (LDPE) ideal for blown film extrusion. Riblene FL 30 is characterized by a good balance between processability, mechanical and optical properties.Films manufactured with Riblene FL 30 are easily heat shrinkable.Main Applications: Riblene FL 30 is recommended for general blown film applications, for the production of low gauge film and shrink film, for lamination and for blend.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.924 g/cc
0.924 g/cc
ISO 1183
Thickness 25.0 - 80.0 microns
0.984 - 3.15 mil
Recommended
Melt Flow 2.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ISO 527-3
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ISO 527-3
Film Elongation at Break, MD 300 %
300 %
ISO 527-3
Film Elongation at Break, TD 650 %
650 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 8.152 g/micron
207.1 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 5.6045 g/micron
142.35 g/mil
ISO 6383-2
Dart Drop Test 125 g
0.276 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ISO 527-3
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ISO 527-3
1% Secant Modulus, MD 180 MPa
26100 psi
ISO 527-3
1% Secant Modulus, TD 190 MPa
27600 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 114 °C
237 °F
Internal method
Vicat Softening Point 93.0 °C

@Load 1.00 kg
199 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746
Optical Properties Metric English Comments
Haze 5.5 %
5.5 %
ISO 14782
Gloss 72 %
72 %
45°; ASTM D2457