- Polimeri Europa Riblene® FF 24 Low Density Polyethylene - Blown Film Extrusion
Polimeri Europa Riblene® FF 24 Low Density Polyethylene - Blown Film Extrusion
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Polimeri Europa (Former EniChem) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa Riblene® FF 24 Low Density Polyethylene - Blown Film Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Riblene FF 24 is a high molecular weight low density polyethylene (LDPE), with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FF 24 is characterized by a good melt strength leading to a good bubble stability during extrusion.Films manufactured with Riblene FF 24 are easily heat shrinkable and characterized by good mechanical properties.Main Applications: Riblene FF 24 is recommended for the production of shrink film for medium loads, for industrial and carrier bags.Information provided by Polimeri Europa.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ISO 1183 |
| Thickness | 40.0 - 150 microns | 1.57 - 5.91 mil | Recommended |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ISO 527-3 |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | 0.11 | 0.11 | ISO 8295 |
| Elmendorf Tear Strength, MD | 2.038 g/micron | 51.77 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 4.076 g/micron | 103.5 g/mil | ISO 6383-2 |
| Dart Drop Test | 280 g | 0.617 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 165 MPa | 23900 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 185 MPa | 26800 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 111 °C | 232 °F | Internal method |
| Vicat Softening Point | 91.0 °C @Load 1.00 kg |
196 °F @Load 2.20 lb |
ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 14 % | 14 % | ISO 14782 |
| Gloss | 45 % | 45 % | 45°; ASTM D2457 |