- Polimeri Europa Riblene® FC 20 Low Density Polyethylene - Blown Film Extrusion
Polimeri Europa Riblene® FC 20 Low Density Polyethylene - Blown Film Extrusion
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Polimeri Europa (Former EniChem) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa Riblene® FC 20 Low Density Polyethylene - Blown Film Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Riblene FC 20 is a high molecular weight low density polyethylene resin (LDPE) suitable for blown film extrusion. Riblene FC 20 is characterized by a high melt strength leading to a good bubble stability during extrusion.Films manufactured by Riblene FC 20 are easily shrinkable and characterized by optimum mechanical properties.Main Applications: Riblene FC 20 is recommended for the production of greenhouse film, heavy duty shrink film and industrial bags.Information provided by Polimeri Europa.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.922 g/cc | 0.922 g/cc | ISO 1183 |
| Thickness | 50.0 - 250 microns | 1.97 - 9.84 mil | Recommended |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.25 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO 527-3 |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 527-3 |
| Film Elongation at Break, TD | 550 % | 550 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 2.038 g/micron | 51.77 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 3.5665 g/micron | 90.589 g/mil | ISO 6383-2 |
| Dart Drop Test | 290 g | 0.639 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 170 MPa | 24700 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 190 MPa | 27600 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 113 °C | 235 °F | Internal method |
| Vicat Softening Point | 93.0 °C @Load 1.00 kg |
199 °F @Load 2.20 lb |
ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 20 % | 20 % | ISO 14782 |
| Gloss | 30 % | 30 % | 45°; ASTM D2457 |