Polimeri Europa Greenflex® FL 25 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Greenflex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Greenflex® FL 25 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Greenflex FL 25 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FL 25 show good optical properties and excellent sealability.Main Applications: Greenflex FL 25 is recommended for the production of lamination film, coextruded films and freezer bags.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.923 g/cc
0.923 g/cc
ISO 1183
Vinyl Acetate Content 4.5 %
4.5 %
Internal Method
Thickness 30.0 - 150 microns
1.18 - 5.91 mil
Recommended
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 96
96
ISO 868/A
Hardness, Shore D 44
44
ISO 868/A
Film Tensile Strength at Yield, MD 7.00 MPa
1020 psi
ISO 527-3
Film Tensile Strength at Yield, TD 7.00 MPa
1020 psi
ISO 527-3
Film Elongation at Break, MD 300 %
300 %
ISO 527-3
Film Elongation at Break, TD 560 %
560 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.20
>= 0.20
ISO 8295
Elmendorf Tear Strength, MD 2.5475 g/micron
64.706 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 3.8722 g/micron
98.354 g/mil
ISO 6383-2
Dart Drop Test 400 g
0.882 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ISO 527-3
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ISO 527-3
1% Secant Modulus, MD 140 MPa
20300 psi
ISO 527-3
1% Secant Modulus, TD 150 MPa
21800 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 103 °C
217 °F
Internal Method
Vicat Softening Point 82.0 °C

@Load 1.00 kg
180 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -80.0 °C
<= -112 °F
ASTM D746
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ISO 14782
Gloss 65 %
65 %
45°; ASTM D2457