Polimeri Europa Greenflex® FD 23 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Greenflex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Greenflex® FD 23 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Greenflex FD 23 is an ethylene vinyl acetate copolymer (EVA) suitable for blown film extrusion. Greenflex FD 23 is a version of Greenflex FD 20 with added slip and antiblocking agents. Films produced with Greenflex FD 23 exhibit good optical properties, high impact resistance, tensile strength, elongation at break and low creep.Main Applications: Greenflex FD 23 is recommended for thermo-shrinkable films for food packaging, including deep-frozen food packaging.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.924 g/cc
0.924 g/cc
ISO 1183
Vinyl Acetate Content 5.0 %
5.0 %
Internal Method
Thickness 50.0 - 200 microns
1.97 - 7.87 mil
Recommended
Melt Flow 0.50 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.50 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 95
95
ISO 868/A
Hardness, Shore D 44
44
ISO 868/A
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ISO 527-3
Film Tensile Strength at Yield, TD 8.00 MPa
1160 psi
ISO 527-3
Film Elongation at Break, MD 450 %
450 %
ISO 527-3
Film Elongation at Break, TD 600 %
600 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.20
>= 0.20
ISO 8295
Elmendorf Tear Strength, MD 2.6494 g/micron
67.295 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 4.076 g/micron
103.5 g/mil
ISO 6383-2
Dart Drop Test 420 g
0.926 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ISO 527-3
Film Tensile Strength at Break, TD 25.0 MPa
3630 psi
ISO 527-3
1% Secant Modulus, MD 120 MPa
17400 psi
ISO 527-3
1% Secant Modulus, TD 125 MPa
18100 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 104 °C
219 °F
Internal Method
Vicat Softening Point 85.0 °C

@Load 1.00 kg
185 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -80.0 °C
<= -112 °F
ASTM D746
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ISO 14782
Gloss 65 %
65 %
45°; ASTM D2457