Polimeri Europa Eraclene® MM 84 U High Density Polyethylene - Injection Molding

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Eraclene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Eraclene® MM 84 U High Density Polyethylene - Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Eraclene MM 84 U is a gas phase high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.Eraclene MM 84 U is characterized by high rigidity and good impact resistance. The resin is UV stabilized and is recommended for the production of items for outdoor exposure.Main Applications: Eraclene MM 84 U is specifically designed for pails and light-weight containers. Moreover, the product is suitable to manufacture dust bins and small industrial containers.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.956 g/cc
0.956 g/cc
ISO 1183
Melt Flow 5.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
14 g/10 min

@Load 5.00 kg,
Temperature 190 °C
14 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 66
66
ISO 868/A
Tensile Strength at Break 20.0 MPa
2900 psi
ISO 527
Tensile Strength, Yield 28.0 MPa
4060 psi
ISO 527
Elongation at Break 550 %
550 %
ISO 527
Flexural Modulus 1.35 GPa
196 ksi
ISO 178
Izod Impact, Notched 1.10 J/cm
2.06 ft-lb/in
ISO 180/A
Thermal Properties Metric English Comments
Melting Point 135 °C
275 °F
Internal method
Vicat Softening Point 127 °C

@Load 1.00 kg
261 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -60.0 °C
<= -76.0 °F
ASTM D746