Polimeri Europa Eraclene® FB 506 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Polimeri Europa (Former EniChem)
Trade Name	Eraclene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa Eraclene® FB 506 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Eraclene FB 506 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully combine excellent performance at high extrusion rates with high film strength and sealability.Main Applications: Eraclene FB 506 can be processed either in blend or in coextrusion. It is possible to use it pure for high rigidity grocery sacks and shopping bags. Usage in blend and/or in coextrusion with LDPE and LLDPE is also recommended for high strength thermo-shrinkable film, as well as for hygienic packaging. The excellent balance between drawability and bubble stability makes Eraclene FB 506 the optimum choice for manufacturing of high quality thin films characterized by outstanding mechanical properties.Information provided by Polimeri Europa.

Physical Properties	Metric	English	Comments
Specific Gravity	0.939 g/cc	0.939 g/cc	ISO 1183
Thickness	10.0 - 50.0 microns	0.394 - 1.97 mil	Recommended
Melt Flow	0.80 g/10 min @Load 5.00 kg, Temperature 190 °C	0.80 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
	20 g/10 min @Load 21.6 kg, Temperature 190 °C	20 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	500 %	500 %	ISO 527-3
Film Elongation at Break, TD	750 %	750 %	ISO 527-3
Elmendorf Tear Strength, MD	1.5285 g/micron	38.824 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	18.342 g/micron	465.89 g/mil	ISO 6383-2
Dart Drop Test	120 g	0.265 lb	F50; ISO 7765-1
Film Tensile Strength at Break, MD	50.0 MPa	7250 psi	ISO 527-3
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ISO 527-3
1% Secant Modulus, MD	400 MPa	58000 psi	ISO 527-3
1% Secant Modulus, TD	500 MPa	72500 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	129 °C	264 °F	Internal method
Vicat Softening Point	119 °C @Load 1.00 kg	246 °F @Load 2.20 lb	ISO 306/A
Brittleness Temperature	<= -60.0 °C	<= -76.0 °F	ASTM D746