Polimeri Europa Eraclene® FA 506 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Eraclene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Eraclene® FA 506 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Eraclene FA 506 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully combine excellent performance at high extrusion rates with high film strength and sealability.Main Applications: Eraclene FA 506 can be processed either in blend or in coextrusion. It is possible to use it pure for high rigidity grocery sacks and shopping bags. Usage in blend and/or in coextrusion with LDPE and LLDPE is also recommended for high strength thermo-shrinkable film, as well as for hygienic packaging. The excellent balance between drawability and bubble stability makes Eraclene FA 506 the optimum choice for manufacturing of high quality thin film characterized by outstanding mechanical properties.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.939 g/cc
0.939 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 0.60 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.60 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
15 g/10 min

@Load 21.6 kg,
Temperature 190 °C
15 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 550 %
550 %
ISO 527-3
Film Elongation at Break, TD 750 %
750 %
ISO 527-3
Elmendorf Tear Strength, MD 2.5475 g/micron
64.706 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 25.475 g/micron
647.07 g/mil
ISO 6383-2
Dart Drop Test 150 g
0.331 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 55.0 MPa
7980 psi
ISO 527-3
Film Tensile Strength at Break, TD 50.0 MPa
7250 psi
ISO 527-3
1% Secant Modulus, MD 400 MPa
58000 psi
ISO 527-3
1% Secant Modulus, TD 500 MPa
72500 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 129 °C
264 °F
Internal method
Vicat Softening Point 119 °C

@Load 1.00 kg
246 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -60.0 °C
<= -76.0 °F
ASTM D746