Polimeri Europa Edistir® PD ICE S 900 High Impact Polystyrene - Very High ESCR

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Grade, Glass Filled
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Edistir®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Edistir® PD ICE S 900 High Impact Polystyrene - Very High ESCR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Very high environmental stress cracking resistant (VH ESCR) HIPS.ICE S 900 exhibits high toughness and excellent chemical resistance to oils, fats and chemical agents, and in particular to cyclopentane. Suitable for extrusion / thermoforming and injection molding.Applications: Designed for inner liners and frames for refrigerators where cyclopentane is used as blowing agent for insulating polyurethane foams. ICE S 900 significantly improves the wall thickness distribution in thermoforming and allows to optimize the thickness of the original extruded sheet.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ISO 1183
Bulk Density 0.650 g/cc
0.0235 lb/in³
ISO 60
Water Absorption <= 0.10 %

@Time 86400 sec
<= 0.10 %

@Time 24.0 hour
ISO 62
Melt Flow 2.5 g/10 min

@Load 5.00 kg,
Temperature 200 °C
2.5 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa
3630 psi
ISO 527
Tensile Strength, Yield 17.5 MPa
2540 psi
ISO 527
Elongation at Break 70 %
70 %
ISO 527
Tensile Modulus 1.45 GPa
210 ksi
ISO 527
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Thickness 4.00 mm
5.23 ft-lb/in²

@Thickness 0.157 in
ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
ASTM D696
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
ISO 8302
Vicat Softening Point 92.0 °C

@Load 5.10 kg
198 °F

@Load 11.2 lb
50°C/h; ISO 306/B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Internal Test
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
IEC 60695-2-1
Shrinkage 0.40 - 0.70 %
0.40 - 0.70 %
Internal Method
Electrical Properties Metric English Comments
Volume Resistivity >= 7.00e+15 ohm-cm
>= 7.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.50e+15 ohm
>= 1.50e+15 ohm
IEC 60093
Dielectric Constant 2.5

@Frequency 50.0 Hz
2.5

@Frequency 50.0 Hz
IEC 60250
Dielectric Strength 65.0 kV/mm
1650 kV/in
IEC 60243
Dissipation Factor 0.00030

@Frequency 50.0 Hz
0.00030

@Frequency 50.0 Hz
IEC 60250
Comparative Tracking Index 500 V
500 V
Solution A; IEC 60112