Polimeri Europa Edistir ICE S 800/N Polystyrene  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Edistir ICE S 800/N Polystyrene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Very high environmental stress cracking resistant (VH ESCR) modified HIPS. ICE S 800/N exhibits high toughness and excellent chemical resistance to oils, fats and chemical agents and in particular to cyclopentane. Designation: Thermoplastics ISO 2897-PS-I,G,093-06-07-12Applications: Designed for inner liners and frames for refrigerators where cyclopentane is used as blowing agent for insulating polyurethane foams. ICE S 800/N significantly improves the wall thickness distribution in thermoforming and allows to optimize the thickness of the original extruded sheet.ICE S 800/N satisfies the norm UL94 HB at 1.5 mm (internal test). This grade in its natural version complies by composition with the requirements set by the main Regulations for plastic materials intended for food contact (including the EEC Directive 90/128 and subsequent amendments). ICE S 800/N is supplied in round pelletsInformation provided by Polimeri EuropaS800/N
Physical Properties Metric English Comments
Bulk Density 0.650 g/cc
0.0235 lb/in³
ISO 60
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Water Absorption <= 0.10 %
<= 0.10 %
24 hours - 23°C; ISO 62
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Internal Method
Melt Flow 4.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
4.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell L 55
55
ISO 2039/2
Tensile Strength at Break 24.5 MPa
3550 psi
50 mm/min; ISO 527
Tensile Strength, Yield 17.5 MPa
2540 psi
50 mm/min; ISO 527
Elongation at Break 70 %
70 %
50 mm/min; ISO 527
Tensile Modulus 1.40 GPa
203 ksi
1 mm/min; ISO 527
Flexural Strength 32.5 MPa
4710 psi
2 mm/min; ISO 178
Izod Impact, Notched 1.10 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.06 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ISO 180/4A
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Thickness 4.00 mm,
Temperature -30.0 °C
2.86 ft-lb/in²

@Thickness 0.157 in,
Temperature -22.0 °F
ISO 180/1A
8.50 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
4.04 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
120°C/h; ASTM D 648
Vicat Softening Point 91.0 °C
196 °F
50 N - 50°C/h; ISO 306/B
100 °C
212 °F
10 N - 50°C/h; ISO 306/A
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
IEC 60695-2-1
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+15 ohm-cm
7.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.50e+15 ohm
1.50e+15 ohm
IEC 60093
Dielectric Constant 2.5

@Frequency 50 Hz
2.5

@Frequency 50 Hz
IEC 60250
Dielectric Strength 65.0 kV/mm
1650 kV/in
IEC 60243
Dissipation Factor 0.00030

@Frequency 50 Hz
0.00030

@Frequency 50 Hz
IEC 60250
Comparative Tracking Index 500 V
500 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 210 - 240 °C
410 - 464 °F
Extrusion
210 - 260 °C
410 - 500 °F
Injection Molding
Mold Temperature 20.0 - 60.0 °C
68.0 - 140 °F
Injection Molding