Polimeri Europa EDISTIR PD RR745E High Impact Polystyrene (HIPS)  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa EDISTIR PD RR745E High Impact Polystyrene (HIPS)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043-1: S/B Designation: Thermoplastic ISO 2897-SB,G,088-03-07-12 Environmental stress cracking resistant (ESCR) HIPS. It combines high impact strength with high chemical resistance to oils, fats and chemical agents. Developed in particular for the fridge sector where hydrocarbons are used as blowing agents for PU insulating foams. This grade is suitable for extrusion/thermoforming and injection molding. Delivered in ropund pellets, this material can be also supplied in cylindrical pellets as Edistir PD RR740E. Applications: Typical applications are inner liners and frames for refrigerators and packaging containers for fatty foods.Unfilled. Suitable for Injection Molding, Sheet Extrusion, Blow Molding, Casting, Thermoforming. Supplied as pellets. Contains release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Melt Flow 4.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
4.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
cm³/10 min
Mechanical Properties Metric English Comments
Tensile Strength, Yield 16.0 MPa
2320 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal
Elongation at Yield 2.0 %
2.0 %
50 mm/min
Tensile Modulus 1.35 GPa
196 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
Vicat Softening Point 90.0 °C
194 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 2.5

@Frequency 100 Hz
2.5

@Frequency 100 Hz
Dielectric Strength 65.0 kV/mm
1650 kV/in
Dissipation Factor 0.00030

@Frequency 100 Hz
0.00030

@Frequency 100 Hz
Comparative Tracking Index 500 V
500 V